Multi-jet fusion for additive manufacturing of radiotherapy immobilization devices: Effects of color, thickness, and orientation on surface dose and tensile strength
Details
Publication Year 2022-04,Volume 23,Issue #4,Page e13548
Journal Title
Journal of Applied Clinical Medical Physics
Publication Type
Research article
Abstract
Immobilization devices are used to obtain reproducible patient setup during radiotherapy treatment, improving accuracy, and reducing damage to surrounding healthy tissue. Additive manufacturing is emerging as a viable method for manufacturing and personalizing such devices. The goal of this study was to investigate the dosimetric and mechanical properties of a recent additive technology called multi-jet fusion (MJF) for radiotherapy applications, including the ability for this process to produce full color parts. Skin dose testing included 50 samples with dimensions 100 mm x 100 mm with five different thicknesses (1 mm, 2 mm, 3 mm, 4 mm, and 5 mm) and grouped into colored (cyan, magenta, yellow, and black (CMYK) additives) and non-colored (white) samples. Results using a 6 MV beam found that surface dose readings were predominantly independent of the colored additives. However, for an 18 MV beam, the additives affected the surface dose, with black recording significantly lower surface dose readings compare to other colors. The accompanying tensile testing of 175 samples designed to ASTM D638 type I standards found that the black agent resulted in the lowest ultimate tensile strength (UTS) for each thickness of 1-5 mm. It was also found that the print orientation had influence on the skin dose and mechanical properties of the samples. When all data were combined and analyzed using a multiple-criteria decision-making technique, magenta was found to offer the best balance between high UTS and low surface dose across different thicknesses and orientations, making it an optimal choice for immobilization devices. This is the first study to consider the use of color MJF for radiotherapy immobilization devices, and suggests that color additives can affect both dosimetry and mechanical performance. This is important as industrial additive technologies like MJF become increasingly adopted in the health and medical sectors.
Keywords
Humans; *Radiometry; Tensile Strength; 3D printing; HP jet fusion 580; cancer treatment; dosimetric testing; medical device manufacture; multi-color; powder bed fusion
Department(s)
Physical Sciences
PubMed ID
35212139
Open Access at Publisher's Site
https://doi.org/10.1002/acm2.13548
Terms of Use/Rights Notice
Refer to copyright notice on published article.


Creation Date: 2024-09-26 05:45:18
Last Modified: 2024-09-26 05:48:04

© 2024 The Walter and Eliza Hall Institute of Medical Research. Access to this website is subject to our Privacy Policy and Terms of Use

An error has occurred. This application may no longer respond until reloaded. Reload 🗙